Low alloy tool steel bar 100CrMn6
Delivery term:The date of payment from buyers deliver within days- Price:
Negotiable
- minimum:
- Total supply:
- Delivery term:
The date of payment from buyers deliver within days
- seat:
Beijing
- Validity to:
Long-term effective
- Last update:
2017-11-17 03:06
- Browse the number:
83
Company Profile
- Shanghai Bozhong Metal Group Co. Ltd By certification [File Integrity]
-
Contact:
bozhong(Ms.)
- Telephone:
-
Area:
Beijing
-
Address:
BUILDING 32#, NO. 518, XINZHUAN ROAD, SONGJIANG, Shanghai, Shanghai, China (201612)
- Website: http://bozhong.clearcutconsult.com/
Product details
Model Number: ZXL127
Brand Name: Baosteel, TISCO
Key Specifications/Special Features:
DescriptionMedium alloy, oil-hardening tooling steel, which is hard-wearing.ApplicationsRoller bearings with thickness up to 50mm.Chemical composition (in weight%)C 0.97
Si 0.60
Mn 1.10
Cr 1.53
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.85
Soft Annealing
Heat to 760-800℃, cool slowly in furnace. This will produce a maximum Brinell hardness of 217.
Normalizing
Normalizing temperature: 860-900℃.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650℃, holding for 1hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden froma temperature of 830-890℃, followed by oil quenching. Hardness after quenching is approx. 64 HRC.
Tempering
Tempering temperature: 150-180℃.
Forging
Hot forming temperature: 1100-850℃.
Specifications:
Grade: 100CrMn6
Standard: DIN, GB
Diameter: 50-500mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy package or as customers’requirements.
Delivery: 7-20 days after received deposit of T/T.
Si 0.60
Mn 1.10
Cr 1.53
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.85
Soft Annealing
Heat to 760-800℃, cool slowly in furnace. This will produce a maximum Brinell hardness of 217.
Normalizing
Normalizing temperature: 860-900℃.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650℃, holding for 1hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden froma temperature of 830-890℃, followed by oil quenching. Hardness after quenching is approx. 64 HRC.
Tempering
Tempering temperature: 150-180℃.
Forging
Hot forming temperature: 1100-850℃.
Specifications:
Grade: 100CrMn6
Standard: DIN, GB
Diameter: 50-500mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy package or as customers’requirements.
Delivery: 7-20 days after received deposit of T/T.
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 7 - 15 days
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe
New Products
-
Most Popular Colors Gel Nail Polish
price: Negotiable
-
Red Color Nail Gel Polish
price: Negotiable
-
Wide Neck PET Jar Stretch Blower Machine
price: Negotiable
-
Active Carbon Filter System
price: Negotiable
-
Steel 1.2601
price: Negotiable
-
Laboratory Weighing Scale
price: Negotiable